Thickness: 0.2-600mm
Width: 20-2200mm
Length: Under 6000mm normally or customized
Weight: 0.5-7.0 tons per pallet or customized
Temper: various Temper (HO-H321)
Surface treatment: mill finished and silvery aluminum plain color
Painting type: PVDF (PPG) and PE(polyester)
Color Coating thickness: Topside of coil :25um (PVDF), 16-25um (PE) Backside of coil:8-10um(PE)
Color code: Solid color as per RAL Code, wood color, marble color, or customized
| Division | Description | Application | Feature |
| 1000 SERIES | 1050 1060 1070 1100 1235representative series aluminum plate is also known as pure aluminum, in the series in 1xxx series belongs to all the alumina quantity of a maximum number of series. Purity can achieve 99.00% above. | Utensil, decoration, Reflecting plate,printing plate, heatproof plate, cookware | Easy to process and weld, resistant to rust,high, conductibility of electricity and heat,low strength |
| 3000 SERIES | 3xxx series aluminum represents 3003 3004,3005, 3 A21 primarily. And can be called in the 3xxx series aluminum antirust aluminum production process more outstanding. The 3xxx series aluminum plate is by manganese as the main component. Content at 1.0-1.5 between. Is a rust-proof function better series. Conventional application in the air conditioning, the refrigerator, such as car in damp environment | Utensil(F/P, inside of rice cooker),aluminum can,material for interior and exterior of building,chemical equipment,Cellular Phone | 20% higher strength than the 1100 series, easily welded and brazed,good antirust,ability Non-heat treatable |
| 5000 SERIES | 5xxx series representatives 5052 5005 5083,5754. The 5000 series aluminum alloy aluminum belong to the more commonly used series, the main elements for magnesium, with magnesium in the amount between 3-5%. And can be called aluminum magnesium alloy. Key features for low density, high tensile strength, elongation rate is high. In the same area under the weight of the magnesium alloy aluminum less than other series. | Ship board heatproof apparatus,material for interior and exterior of building,Parts of Electronic tools.Automobile Components | Excellent corrosion resistance andweld ability together with Easy to process and weld and superior hardness &heatproofCan be anodized for increased corrosion resistance |
| 6000 SERIES | 6xxx series represents 6061 mainly contain magnesium and silicon of two elements, so focused on the 4000 series and the advantages of the 5000 series 6061 is a cold treatment aluminum forging products, apply to fight against corrosion, oxidizing demanding applications. | IT equipment & facility, Mould material,motor material, automatic line,machine & plant etc | Easy to process , good corrosion resistance, high toughness and processed without distortion after heat-treatable, superior surface treatment |
| 7000 SERIES | 7000 aluminum alloy is another common alloy, wide variety. It contains zinc and magnesium. The best strength in the common aluminum alloy is 7075 alloy, but it can't be welded, and its corrosion resistance is rather poor, many manufacturing parts with CNC cutting is 7075 alloy. | The aerospace industry & High strength accessories | 7000 series is high tensile to process with special alloy |
| Chemical Composition % |
| Alloy No. | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | V | Ti | Zr | Al |
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | - | - | 0.05 | 0.05 | 0.03 | - | Remainder |
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | - | 0.05 | 0.05 | 0.03 | - | Remainder |
| 1070 | 0.2 | 0.25 | 0.04 | 0.03 | 0.03 | - | - | 0.04 | 0.05 | 0.03 | - | Remainder |
| 1100 | 0.45 | 0.35 | 0.05-0.20 | 0.03 | - | - | - | 0.01 | 0.05 | - | - | Remainder |
| 2014 | 0.50-1.20 | 0.7 | 3.9-5.0 | 0.4-1.2 | 0.2-0.8 | 0.1 | - | 0.25 | - | 0.15 | - | Remainder |
| 2017 | 0.20-0.80 | 0.7 | 3.5-4.5 | 0.40-1.0 | 0.4-0.8 | 0.1 | - | 0.25 | - | 0.15 | - | Remainder |
| 2024 | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.1 | - | 0.25 | - | 0.15 | - | Remainder |
| 3003 | 0.6 | 0.7 | 0.05-0.20 | 1.0-1.5 | - | - | - | 0.1 | - | - | - | Remainder |
| 3004 | 0.3 | 0.7 | 0.25 | 1.0-1.5 | 0.8-1.3 | - | - | 0.25 | - | - | - | Remainder |
| 3105 | 0.6 | 0.7 | 0.3 | 0.3-0.8 | 0.2-0.8 | 0.2 | - | 0.4 | - | 0.1 | - | Remainder |
| 5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | - | 0.25 | - | - | - | Remainder |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | - | 0.1 | - | - | - | Remainder |
| 5083 | 0.4 | 0.4 | 0.1 | 0.40-1.0 | 4.0-4.9 | 0.05-0.25 | - | 0.25 | - | 0.15 | - | Remainder |
| 5086 | 0.4 | 0.5 | 0.1 | 0.2-0.7 | 3.5-4.5 | 0.05-0.25 | - | 0.25 | - | 0.15 | - | Remainder |
| 5182 | 0.2 | 0.35 | 0.15 | 0.2-0.5 | 4.0-5.0 | 0.1 | - | 0.25 | - | 0.1 | - | Remainder |
| 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | - | 0.2 | 0.1-0.6Mn+Zn | 0.15 | - | Remainder |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | - | 0.25 | - | 0.15 | - | Remainder |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.90 | 0.1 | - | 0.1 | - | 0.1 | - | Remainder |
| 6082 | 0.7-1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6-1.2 | 0.25 | - | 0.2 | - | 0.1 | - | Remainder |
| 7005 | 0.35 | 0.4 | 0.1 | 0.2-0.7 | 1.0-1.8 | 0.06-0.20 | - | 4.0-5.0 | - | 0.01-0.06 | 0.08-0.20 | Remainder |
| 7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | - | 5.1-6.1 | - | 0.2 | - | Remainder |
| 7175 | 0.15 | 0.2 | 1.2-2.0 | 0.1 | 2.1-2.9 | 0.18-0.28 | - | 5.1-6.1 | - | 0.1 | - | Remainder |
| 8011 | 0.50-0.90 | 0.6-1.0 | 0.1 | 0.2 | 0.05 | 0.05 | - | 0.1 | - | 0.08 | - | Remainder |
| 8021 | 0.15 | 1.2-1.7 | 0.05 | - | - | - | - | - | - | - | - | Remainder |
| 8079 | 0.05-0.3 | 0.7-1.3 | 0.05 | - | - | - | - | 0.1 | - | - | - | Remainder |
Performance
1) Long life, lower cost, but has high cost for recovery ;
2) High plasticity, corrosion resistance, electrical conductivity and thermal conductivity, acceptable for contact welding, gas welding;
3) Xinyu Non-ferrous Metal Ltd has a strict control of product and processing, composition to ensure the product performance reached the international advanced level;
The performance of PE color coated coil
1) Thickness≤0.5mm
| Item | Test Item | Standard | National standard | Test Result |
| 1 | Color Difference | ECCA T3 | ΔE≤2.0 | ΔE≤1.5 |
| 2 | Gloss Difference | ECCA T2 | ≤10 | ≤5 |
| 3 | Coating Thickness | ECCA T1 | Min 14µm | ≥16µm |
| 4 | Pencil Hardness | ASTM D3363 | ≥HB | HB |
| 5 | T-bend | ASTM D4145 | ≤3T | ≤2T |
| 6 | Adhesion | ASTM D3359 | Grade 0 | Grade 0 |
| 7 | Impact | ASTM D2794 | ≥20kg.cm | ≥20kg.cm |
| 8 | Boiling water Resistance | GB/T17748 | 2h no change | 2h no change |
| 9 | Solvent Resistance | ASTM D2248 | 200 times paint remaining | 200 times paint remaining |
| 10 | Salt Resistance | ASTM B117 | 720 hrs≤grade 1 | 720hrs≤grade 1 |
| 11 | Dirt Resistance | GB/T9780 | ≤5% | <5% |
| 12 | Color retaining | GB/T16259 | 600hrs △E≤2.0 | △E≤2.0 |
| 13 | Gloss weaken Level | 600hrs ≤ grade 2 | 600hrs ≤ grade 2 |
| 14 | Chalking | 600hrs No Change | No Change |
2) The performance of PVDF color coated coil | Item | Test Item | Standard | National standard | Test Result |
| 1 | Color Difference | ECCA T3 | ΔE≤2.0 | ΔE≤1.5 |
| 2 | Gloss Difference | ECCA T2 | ≤10 | ≤5 |
| 3 | Coating Thickness | ECCA T1 | Two layers Min 23μm | ≥25μm |
| Three layers Min 30μm | ≥34μm |
| 4 | Pencil Hardness | ASTM D3363 | ≥HB | HB |
| 5 | T-bend | ASTM D4145 | ≤2T | ≤2T |
| 6 | Adhesion | ASTM D3359 | Grade 0 | Grade 0 |
| 7 | Impact | ASTM D2794 | ≥50kg.cm | ≥50kg.cm |
| 8 | Boiling water Resistance | GB/T17748 | 2h No change | 4h No change |
| 9 | Solvent Resistance | ASTM D2248 | 200 times paints remaining | 500 times no break |
| 10 | Acidity Resistance | ASTM D1308 | 5%HCL 24hrs No change | No change |
| 11 | Alkali Resistance | ASTM D1308 | 5%NaOH 24hrs No change color △E≤2.0 | No change |
| 12 | Nitric acid Resistance | AAMA620 | △E≤5.0 | △E≤5.0 |
| 13 | Oil Resistance | ASTM D1308 | 20#oil 24hrs No change | No change |
| 14 | Salt Spray Resistance | ASTM B117 | 4000hrs ≤Grade 1 | No change |
| 15 | Abrasion resistance | ASTM D968 | ≥5L/μm | ≥5L/μm |
| 16 | Dirt Resistance | GB/T9780 | ≤5% | <5% |
| 17 | Color retaining | GB/T16259 | 4000 hrs△E≤4.0 | 4000 hrs △E≤3.0 |
| 18 | Gloss weaken Level | 4000 hrs ≤ Grade 2 | 4000 hrs ≤ Grade 2 |
| 19 | Chalking | 4000 hrs No change | 4000 hrs No change |